Product Name
|
type
|
Solid content%
|
PH
|
Viscosity,
Cps@25 C
|
MFT,℃
|
TG,℃
|
application
|
The characteristics of the product
|
|
CFA-77
|
Pure acrylic emulsion
|
45
|
7-9
|
30-100S
|
|
7
|
Emulsion of low VOC, no three benzene residue, meet the requirements of tobacco packaging industry
|
Pack light oil coating, direct plating paper
|
|
CFA-100
|
Pure acrylic emulsion
|
45
|
7-9
|
30-100S
|
|
100
|
Hard emulsion, low VOC, no three benzene residue
|
Pack light oil coating, direct plating paper
|
|
CFA-79
|
Styrene acrylic emulsion
|
45
|
7-9
|
30-100S
|
|
40
|
|
Recommended dry metal paint
|
|
|
The metal attached, water resistance, salt fog resistance
|
|
CFA-78
|
Acrylic emulsion
|
45
|
6-8
|
|
|
|
Since the stem rust primer
|
Good acid resistance, can be directly added phosphate, metal adhesion
|
|
CFA-76
|
Modified acrylic emulsion
|
45
|
7-9
|
|
|
|
Recommended PU runway
|
Hydroxy functional, good toughness, wear resistance, high hardness
|
|
CFA-75
|
Modified acrylic emulsion
|
45
|
7-9
|
|
|
|
Recommended metal, glass paint.
|
With amino collocation, good adhesion, good stability of silver
|
|
CFA-74
|
Acrylic acid solution
|
45
|
7-9
|
|
|
|
Recommended paint bottle
|
With a good amino collocation, dense, high liquor, boiling water resistance
|
|
CFA-73
|
Acrylic acid solution
|
45
|
7-9
|
|
|
|
Aluminum leaching e-coatings
|
With good adhesion, amino collocation, weather resistance, salt fog resistance
|
|
CFA-72
|
Acrylic emulsion
|
45
|
7-9
|
|
|
|
Recommended Wood Coatings
|
|
|
Hydroxyl, dual curing, high gloss; early high hardness, fast drying.Single and double component are suitable
|
|
|
|
|
|
|
|
|
|
|
|
|
CFE-50
|
Emulsification epoxy
|
50
|
7-8
|
500-1000
|
|
|
Recommended container coatings
|
Good adhesion, salt fog, show good color, good operation stability
|
|
CFE-51
|
|
The outer emulsified waterborne epoxy resin
|
|
|
55
|
6-8
|
100-500
|
Epoxy equivalent 350-360
|
|
Suitable for hospitals and other engineering floor, glass and metal paint
|
Ions with good stability, can be at room temperature but also with amine crosslinking, acid curing crosslinking of low VOC emission collocation; less than 10G/L.
|
|
CFE-20
|
|
The outer emulsified waterborne epoxy resin
|
|
|
55
|
6-8
|
200-1000
|
Epoxy equivalent 920-980
|
|
Floor paint, metal anti-corrosion paint
|
Particle with good stability, can be at room temperature and crosslinking amine curing agent, curing temperature and acid can also be collocation; low VOC emissions, less than 60g/L
|
|
|
|
|
|
|
|
|
|
|
|
CFP-80
|
Water soluble polyester
|
80
|
|
Z5-Z6
|
|
|
Water of high-grade coil coatings
|
High gloss, high weathering resistance, boiling water resistance, good toughness, up to 1T
|
|
|
|
|
|
|
|
|
|
|
|
CFU-801
|
|
50
|
7-8
|
|
|
|
Waterborne wood paint
|
High hardness, good water resistance, high gloss, good chemical resistance
|
|
CFU-802
|
|
50
|
7-8
|
|
|
|
Leather finishing agent, printing paste
|
High temperature, high elongation
|
|
CFU-803
|
|
60
|
7-8
|
|
|
|
Soft packaging ink
|
The composite has high strength, good pigment dispersion
|
|
CFU-803Y
|
|
50
|
7-8
|
|
|
|
Leather finishing agent, printing paste.
|
Aromatic, high light and high solid content, high fullness.
|
|
CFU-804
|
|
50
|
7-8
|
|
|
|
PVC composite material, adhesive
|
Strong adhesive force
|
|
CFU-805
|
|
50
|
7-8
|
|
|
|
Water transfer coating
|
Aliphatic polyurethane, high hardness
|
|
CFU-806
|
|
30
|
7-8
|
|
|
|
Dumb light oil film
|
Water soluble matting resin, high hardness water resistance
|
|
|
|
|
|
|
|
|
|
|
|
CF-100
|
Pyridine nitrogen
|
|
|
|
|
|
Light color, low odor, high efficiency
|
Used in aqueous PU or crosslinked acrylic acid, improve the water resistance, improve the adhesion, improve film strength
|
| 中文版 